| Material Properties |
Solidus |
°C |
217 |
| Liquidus |
°C |
228 |
| Hardness |
HV |
14.1 |
| Density |
g/cc |
7.33 |
| Specific Heat Capacity |
J/kg °C |
0.17 |
| Stress at Max Load (Mean) |
N/mm² |
29.5 |
| Elongation at Failure (Mean) |
% |
21.8 |
| Thermal Expansion (30–100°C) |
x10⁻⁶ /°C |
1.79 |
| Thermal Expansion (100–150°C) |
x10⁻⁶ /°C |
2.30 |
| Silver Content |
% |
0.3 ±0.15 / -0.05 |
| Copper Content |
% |
0.70 ±0.1 |
| Lead Content |
% |
Max 0.03% |
| Recommended Process Settings |
Single Wave – Pot Temperature |
°C |
255–265 |
| Single Wave – Conveyor Speed |
m/min |
1.0–1.5 |
| Single Wave – Contact Time |
sec |
2.3–2.8 |
| Dual Wave – Pot Temperature |
°C |
255–265 |
| Dual Wave – Conveyor Speed |
m/min |
1.0–1.5 |
| Dual Wave – Contact Time |
sec |
3.0–3.5 |